What is the density of 17-4 stainless steel?
What is the density of 17-4 stainless steel?
7.75 g/cm3
Grade 17-4 stainless steel is the most widely used steel of the precipitation hardening grade steels. It has high toughness, strength, and corrosion resistance….Physical Properties.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 7.75 g/cm3 | 0.280 lb/in³ |
What is 17 7PH steel?
A stable, chromium-nickel-aluminum steel, 17-7 is a precipitation hardening steel with a high strength and moderately resistant to corrosion. In terms of corrosion resistance, 17-7 PH is comparable to 304 stainless steel and a better choice when compared to the 400 series of stainless steel.
How do you heat treat 17-4 to H900?
The AL 17-4 Precipitation Hardening Alloy is furnished in the annealed condition. This is also called the solu- tion heat treated condition, or Condition A. Annealing is conducted by heat treating at approximately 1900°F (1040°C) to 1950°F (1065°C) and cooling to room tem- perature.
What are the physical properties of 17 7ph stainless steel?
Stainless steel grade 17-7 PH is a precipitation hardened stainless steel that possesses high strength and hardness, excellent fatigue properties, good formability, good corrosion resistance, and minimal distortion upon heat treatment. The properties of this alloy are well suited for aerospace applications.
What kind of stainless steel is 17-4 PH?
17-4 PH is a martensitic, precipitation-hardening stainless steel that provides an outstanding combination of high strength and hardness along with excellent corrosion resistance.
What are the mechanical properties of alloy 17-4 PH?
Alloy 17-4PH | Material Datasheet 17-4 PH Steel contains 4% copper and may be hardened by a single low temperature precipitation hardening heat treatment, producing excellent mechanical properties at a high strength level. 17-4 PH provides this high strength in combination with good mechanical properties at temperatures of up to 600°F (316°C).
When to heat treat alloy 17-4PH h1150?
Cool forgings to below 90°F to ensure grain refinement. Alloy 17-4 is limited to mild operations since in the annealed (solution treated) condition the material is hard. For severe cold working the material should be heat treated to condition H1150. This will help prevent possible cracking. Bend radius in excess of 7T is often required.
What are the properties of 17-4PH steel?
As supplied 17-4PH is usuall in the solution treated condition (Condition A). It can be heat treated at different temperatures to offer a wide range of properties. (We also hold stock in H1150+H1150, and annealed block). 363 max. 39 max. . The material does not have direct Metallography properties. Directory is being updated.